PULSE™ 6000 BG
| Category: | PC+ABS , PC/ABS Engineering Resin |
| Manufacturer: | Trinseo |
| Trademark: | PULSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LtgIXP_PULSE-6000-BG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PULSE 6000 BG is a PC/ABS resin offering an interesting combination of heat ageing characteristics, low temperature impact performance and high melt strength. Its low MFR enables manufacturing of complex blow molding parts. Typical applications for this product are Blow Molded Spoilers, knee bolsters and Seat Backs. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.53 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 2160 | MPa | ASTM D638 |
| -- | 2280 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield | 51.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2 |
| Break | 54.5 | MPa | ASTM D638 |
| Break | 53.0 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | > 80 | % | |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 50 | kJ/m² | |
| 23°C | 61 | kJ/m² | |
| Notched Izod Impact | |||
| -40°C | 640 | J/m | ASTM D256 |
| 23°C | 750 | J/m | ASTM D256 |
| -40°C | 61 | kJ/m² | ISO 180/4A |
| 23°C | 69 | kJ/m² | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 111 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ISO 306/A120 |
| -- | 130 | °C | ISO 306/B50 |
| CLTE - Flow (-40 to 82°C) | 7.4E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOLEN H451 IM | SIBUR, LLC | PP Homopolymer | TOLEN |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 1600 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| Crastin® SK642FR NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Durethan® AC 30 DUS027 000000 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |
| Petrothene® GA601 | LyondellBasell Industries | LLDPE | Petrothene® |