Greenflex® FD 50
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Greenflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LsXWH3_GreenflexFD50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Greenflex FD 50 is an ethylene vinyl acetate copolymer resin (EVA) for blown film extrusion. Films produced by Greenflex FD 50 exhibit good optical and sealing properties, high flexibility and toughness. Greenflex FD 50 is recommended for the production of agricultural films and water proofing membrane having outstanding mechanical performances (flexibility, elasticity and adherence) and dimensional stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 17.0 | wt% | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, Injection Molding | 90 | ISO 868 | |
| Shore D, Injection Molding | 39 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 30 to 150 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% sectioning, MD : Blown film | 55.0 | MPa | ISO 527-3 |
| 1% sectioning, TD : Blown film | 60.0 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : yield, blow film | 4.50 | MPa | ISO 527-3 |
| TD : yield, blow film | 4.00 | MPa | ISO 527-3 |
| MD : fracture, blow film | 35.0 | MPa | ISO 527-3 |
| TD : fracture, blow film | 30.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : fracture, blow film | 450 | % | ISO 527-3 |
| TD : fracture, blow film | 700 | % | ISO 527-3 |
| Dart Drop Impact 1(Blown Film) | > 700 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 20.0 | kN/m | ISO 6383-2 |
| TD | 44.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 67.0 | °C | ISO 306/A |
| Melting Temperature | 88.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 83 | ASTM D2457 | |
| Haze (Blown Film) | 1.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PE HD1090 | Qenos Pty Ltd | HDPE | Qenos PE |
| Sicoflex FP454 | Ravago Group | ABS | Sicoflex |
| Sylvin 8475-85UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Xuchuan XCW-8130 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| LNP™ THERMOCOMP™ DX13006 compound | SABIC Innovative Plastics Europe | PC | LNP™ THERMOCOMP™ |