PLUSTEK RA300G6
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LrwOf9_PLUSTEK-RA300G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS-FIBER REINFORCED POLYAMIDE 66 FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 - 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 - 0.30 | % | ASTM D955 |
| -- | 0.20 - 0.30 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 6.6 | % | ASTM D570 |
| Saturated, 23°C | 6.6 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.6 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | > 150 | MPa | ASTM D638 |
| Yield | > 160 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 3.0 | % | ASTM D638 |
| Fracture | > 3.0 | % | ISO 527-2 |
| Flexural Modulus | > 7500 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | > 210 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | > 75 | J/m | ASTM D256 |
| 23°C | > 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 259 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 249 | °C | ASTM D648, ISO 75-2/A |
| Maximum operating temperature- Short Peaks Operation | 200 | °C | |
| Maximum Continuous Use Temperature | 100 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | 3 | mm/min | FMVSS 302 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 90 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.50 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Mold Temperature | 65.0 - 110 | °C | |
| Injection Pressure | 70.0 - 125 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 22460 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Cosmic DAP K66/6230F | Cosmic Plastics, Inc. | DAP | Cosmic DAP |
| ELASTOSIL® FLR 3900/40 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® FLR |
| Sylvin 2900-80 Clear 8391 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9302-70 WHITE 1264 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |