Braskem PE ML2400N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LrbQX5_Braskem-PE-ML2400N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The resin ML2400N is a Linear Low Density Polyethylene, 1-butene based, with good flexibility and low warpage. Without slip agent. Narrow molecular weight distribution. Applications: Masterbatches; High productivity injection of pigmented closures; Housewares. Processing Conditions: This resin was developed to be injected under conditions comparable to polyethylene resins with similar melt index and density range. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.926 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 2.00 mm, 10% Igepal, Compression Molded, F50) | 1.50 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 49 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 12.0 | MPa | |
| Break, Compression Molded | 11.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, Compression Molded | 16 | % | |
| Break, Compression Molded | 340 | % | |
| Flexural Modulus - 1% Secant (Compression Molded) | 415 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 46.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 150 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 MRGV 25/15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| DJSilicone NE-151 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| FERREX® GPP20CF54UL-WH | Ferro Corporation | PP, Unspecified | FERREX® |
| Hanwha Total PP BJ550 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| LNP™ COLORCOMP™ E1000 compound | SABIC Innovative Plastics Europe | PEI | LNP™ COLORCOMP™ |