POCAN® B 1300 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS Corporation |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LqWonG_POCANB1300000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, non-reinforced, injection molding, extrusion |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 45.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 260°C, 3.00mm 1 | 1.9 | % | ISO 2577 |
| Vertical flow direction : 150°C, 1 hour, 3.00mm 2 | 0.50 | % | ISO 2577 |
| Flow direction : 260°C, 3.00mm 3 | 1.9 | % | ISO 2577 |
| Flow direction : 150°C, 1 hour, 3.00mm 4 | 0.50 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 105.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 8.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 20 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2400 | MPa | ISO 899-1 |
| 1000 hr | 1400 | MPa | ISO 899-1 |
| Flexural Modulus 5(23°C) | 2700 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% strain, 23°C | 75.0 | MPa | ISO 178/A |
| 23°C 6 | 90.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 6.0 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion (23°C) | A 1 | IEC 60426 | |
| ISO Shortname | PBT, GN, 10-030 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 150 | kJ/m² | ISO 179/1eU |
| 23°C | 220 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 150 | kJ/m² | ISO 180/1U |
| 23°C | 150 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 15.0 | J | ISO 6603-2 |
| 23°C, energy to peak power | 110 | J | ISO 6603-2 |
| 23°C | 40.0 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (-30°C) | 3860 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 45.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 180 | °C | ISO 306/B50 |
| Ball Pressure Test (190°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.25 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C, 1.00 mm) | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.40 | IEC 60250 | |
| 23°C, 1 MHz | 3.20 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| Solution a | 600 | V | IEC 60112 |
| Solution B | 275 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index 9 | 24 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 600 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 600 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9150 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Telcar® TL-1472A | Teknor Apex Company | TPE | Telcar® |
| Trademark PP PPC2040M | Trademark Plastics Corporation | PP Impact Copolymer | Trademark PP |
| Niuk 20RN00 | Shanghai Niuk New Plastic Technology Co., Ltd. | ABS | Niuk |
| Chiao Fu PA66 MD212G43 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |