ACCUTECH™ CP0437C20L
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LpnsVI_ACCUTECH-CP0437C20L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™CP0437C20L is a polypropylene copolymer (PP Copoly) product, which contains a 20% calcium carbonate filler. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 50 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 14.0 | MPa | ASTM D638 |
| Fracture | 12.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 | % | ASTM D638 |
| Fracture | 90 | % | ASTM D638 |
| Flexural Modulus | 1000 | MPa | ASTM D790 |
| Flexural Strength | 16.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 560 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 50.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 75.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP640V | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| X-Pro SP 200 TF 13 3325 | CTC Plastics, LLC | PP Copolymer | X-Pro |
| NuSil MED10-6605 | NuSil Technology | Silicone | NuSil |
| CompaMid® PA 6.6 HI | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| Hax™ HFX 509 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |