Plexiglas® 7M
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Lnw6MW_Plexiglas-7M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Profile: PLEXIGLAS® 7M is based on polymethyl methacrylate (PMMA). Besides showing the familiar properties of PLEXIGLAS® 7H molding compounds, such as
PLEXIGLAS® 7M is special in that it
Application: PLEXIGLAS® 7M is particularly suitable for extruding profiles and panels for use in lighting engineering. Examples: lighting fixtures, displays and similar extruded items for technical purposes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 2.90 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 69.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 108 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 104 | °C | ISO 306/B50 |
| CLTE - Flow (0 to 50°C) | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance 1 | 92.0 | % | ISO 13468-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 94.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Melt Temperature | 220 to 260 | °C | |
| Die Temperature | 220 to 260 | °C |
| Note Message | |
|---|---|
| 1 . | D65 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2825 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TAISOX 6810M | Formosa Plastics Corporation | LDPE | TAISOX |
| Thermoset Plastics EP-236 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| ACCUTECH™ CP0437G20M10CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| BCC Resins BC 5200 | BCC Products Inc. | Epoxy | BCC Resins |