PRL TP-G15
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LnRxRz_PRL-TP-G15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL TP-G15 is a Polybutylene Terephthalate (PBT) product filled with 15% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.0 to 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 93.1 | MPa | |
| Break, 3.18 mm | 93.1 | MPa | |
| Flexural Modulus (3.18 mm) | 4830 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 204 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 188 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stretchene RP1903 | LyondellBasell Industries | PP Random Copolymer | Stretchene |
| TATREN® IM 22 63 | Slovnaft Petrochemicals, s.r.o. | PP Impact Copolymer | TATREN® |
| ELIX™ ABS M205FC | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Globalene® PC366-3 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| Plenco 02300 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |