MARCOBLEND AU 2000
| Category: | PC , Polycarbonate |
| Manufacturer: | POLY GIN |
| Trademark: | MARCOBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ln7I1v_MARCOBLEND-AU-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MARCOBLEND AU2000 is an ignition resistant and glass fiber reinforced polycarbonate resin. The resin is Halogen free and compliance with TCO and RoHS certification. The unique characters include superior processability, good stiffness, and excellent dimension stability and suitable for use in TFT LCD frame and internal structure parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 69.0 | MPa | ASTM D638 |
| Flexural Modulus | 3390 | MPa | ASTM D790 |
| Flexural Strength | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 145 | °C | |
| 1.8 MPa, Unannealed | 127 | °C | |
| CLTE | ASTM D696 | ||
| Flow | 4.0E-5 | cm/cm/°C | |
| Transverse | 6.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 260 to 265 | °C | |
| Middle Temperature | 265 to 270 | °C | |
| Front Temperature | 270 to 275 | °C | |
| Nozzle Temperature | 275 to 280 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PA 1406 | Premix Oy | Nylon 6 | PRE-ELEC® |
| Elastollan® 1174 D | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| Karina GRAY MBU -E 18/ 15-IE-HSF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OnForce™ LFT NN-30LCF/002 Grey | PolyOne Corporation | Nylon 66 | OnForce™ LFT |
| 3M™ Dyneon™ PTFE Compound PDR 08004 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |