Vyncolit SI 9002 is a silicone (Silicone) material, and its filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing methods are: resin transfer molding, compression molding or injection molding. The main characteristics of Vyncolit SI 9002 are: impact resistance. Typical application areas include: Electrical/electronic applications Wire and cable military applications

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Impact resistance, high Good electrical performance
Uses	Electronic insulation Military application Connector
Forms	Particles
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.10	g/cm³	ASTM D792
Bulk Factor	1.9		ASTM D1895
Molding Shrinkage - Flow (Transfer Molded)	0.50 - 0.80	%	ASTM D955
Water Absorption (23°C, 24 hr)	0.16	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	90		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	27.6	MPa	ASTM D638
Flexural Modulus	13800	MPa	ASTM D790
Flexural Strength	51.7	MPa	ASTM D790
Compressive Strength	87.9	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	21	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	288	°C	ASTM D648
CLTE - Flow	3.3E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength			ASTM D149
-- ¹	9.4	kV/mm	ASTM D149
-- ²	8.9	kV/mm	ASTM D149
Arc Resistance	210	sec	ASTM D495

Injection	Nominal Value	Unit
Middle Temperature	71.1 - 82.2	°C
Nozzle Temperature	82.2 - 93.3	°C
Processing (Melt) Temp	93.3	°C
Mold Temperature	132 - 154	°C
Injection Pressure	41.4 - 82.7	MPa
Holding Pressure	20.7 - 41.4	MPa
Back Pressure	0.345	MPa

Injection instructions
Cure Time, 0.125 in: 45 secWater Absorption, ASTM D570, 48 hrs, 50°C: 0.39%Dielectric Strength, ASTM D149, 60 Hz, Method A, wet: 240 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 225 V/milBulk Factor, ASTM D1895: 1.9 to 1.95Compression and Transfer Molding Conditions: Preheat Temperature: 180 to 200 °F Mold Temperature: 280 to 300 °F Compression Mold Pressure: 2000 to 8000 psi Transfer Mold Pressure: 4000 to 8000 psi Cure Time, 0.125 in: 180 sec

Injection instructions

Cure Time, 0.125 in: 45 secWater Absorption, ASTM D570, 48 hrs, 50°C: 0.39%Dielectric Strength, ASTM D149, 60 Hz, Method A, wet: 240 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 225 V/milBulk Factor, ASTM D1895: 1.9 to 1.95Compression and Transfer Molding Conditions: Preheat Temperature: 180 to 200 °F Mold Temperature: 280 to 300 °F Compression Mold Pressure: 2000 to 8000 psi Transfer Mold Pressure: 4000 to 8000 psi Cure Time, 0.125 in: 180 sec

Note Message
1 .	Method A (short time)
2 .	Method B (step by step)

Category:	Silicone , Silicone
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LkIv0S_Vyncolit-SI-9002.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Matrixx 90N5356	The Matrixx Group, Inc.	PC+ABS	Matrixx
REPOL® B550MN	Reliance Industries Limited	PP Impact Copolymer	REPOL®
Royalstat R635	Spartech Plastics	ABS	Royalstat
Verolloy B6528	PlastxWorld Inc.	ABS+PBT	Verolloy
Durethan® BKV 130 CS DUS008 600091	LANXESS GmbH	Nylon 6	Durethan®