| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LgZcMp_RTP-1305-EF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13100 | MPa | ASTM D638 |
| Tensile Strength | 117 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.1 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Compressive Strength | 152 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 320 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 260 | °C | ASTM D648 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.30 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 14 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 4mil/in.The value listed as flammability, UL 94, was tested in accordance with RTP test standards.This material is resistant to heat and can be used in low load applications operating up to 500 F. Strengths and chemical resistance are excellent and the material is flame retardant. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 302 - 343 | °C | |
| Middle Temperature | 302 - 343 | °C | |
| Front Temperature | 302 - 343 | °C | |
| Mold Temperature | 65.6 - 177 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 FR | RTP Company | ABS | RTP |
| tefabloc® TP SD 333 75A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| NANCAR® 1203LD | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| NEOPLAST 145 FT EB | Zylog Plastalloys | TPV | NEOPLAST |
| Eastar™ AN011, Natural | Eastman Chemical Company | Copolyester | Eastar™ |