Sasol Polymers PE HR411/06

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Sasol Polymers
Trademark:	Sasol Polymers PE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Lg25wV_Sasol-Polymers-PE-HR411-06.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Features

High rigidity

Excellent impact strength

Excellent chemical resistance

Good ESCR

Tough and abrasion resistant

Colourable

Powder

Hexene copolymer

Applications

Large mouldings

Articles for indoor use

General Information
Additive	Antioxidant
Features	Antioxidant Copolymer Food Contact Acceptable Good Abrasion Resistance Good Chemical Resistance Good Colorability Good Toughness Hexene Comonomer High ESCR (Stress Crack Resist.) High Impact Resistance High Rigidity
Agency Ratings	FDA 21 CFR 177.1520
Forms	Powder
Processing Method	Rotational Molding

Physical	Nominal Value	Unit	Test Method
Density	0.939	g/cm³	ASTM D1505
Apparent Density	0.33	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	3.5	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (100% Igepal CO-630, F50)	> 500	hr	ASTM D1693
Particle Size (< 600.0 µm)	90.0	%	ASTM D1921

Thermal	Nominal Value	Unit	Test Method
Impact Test ¹(-40°C)	350	J/cm	ASTM D3029

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	61		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ²			ASTM D638
Yield	19.0	MPa
Break	24.0	MPa
Tensile Elongation ³(Break)	820	%	ASTM D638
Flexural Modulus	846	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	121	°C	ASTM D1525

Injection	Nominal Value	Unit
Processing (Melt) Temp	270 to 300	°C

Note Message
1 .	Tested on rotomoulded product
2 .	50 mm/min
3 .	50 mm/min

Resin Grade	Manufacturer	Category	Trademark
MARPOL® COPP 50.1.8	Marco Polo International, Inc.	PP Copolymer	MARPOL® COPP
RTP 300 TFE 10 FR	RTP Company	PC	RTP
SUPREME HIPS SH400M	Supreme Petrochem Ltd.	PS (HIPS)	SUPREME HIPS
DuraGrip® DGR 6040NCEHT	Advanced Polymer Alloys	TPE	DuraGrip®
Karina RED PVC COMPOUND TR-500D42/225-B-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina