Sarlink® TPE FM-2676 (PRELIMINARY DATA) Datasheet,TPE,Teknor Apex Company-SHANGHAI SUSHENG

Message
Sarlink FM-2676 is a general purpose thermoplastic elastomer, available in NAT, BLK, and colors, designed for automotive interior applications, including floor mats. Sarlink FM-2676 is a medium hardness, high density, filled grade suitable for extrusion and thermoforming.

General Information
Features	Workability, good Good flexibility Good tear strength Good coloring Good adhesion Low liquidity Good chemical resistance Good wear resistance Good weather resistance Good toughness Fill Medium density Medium hardness
Uses	Thermoforming Applications Application in Automobile Field Car interior parts Rubber substitution
RoHS Compliance	RoHS compliance
Appearance	Available colors Natural color
Forms	Particle
Processing Method	Extrusion Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	1.10	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	0.40	g/10 min	ASTM D1238

Hardness	Nominal Value	Test Method
Durometer Hardness		ISO 868
Shore A, 1 second, injection molding	79	ISO 868
Shore A, 5 seconds, injection molding	77	ISO 868
Shore A, 15 seconds, injection molding	75	ISO 868

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹			ISO 37
Transverse flow : 100% strain	2.53	MPa	ISO 37
Flow : 100% strain	3.75	MPa	ISO 37
Tensile Stress ²			ISO 37
Transverse flow : Fracture	9.20	MPa	ISO 37
Flow : Fracture	6.30	MPa	ISO 37
Tensile Elongation ³			ISO 37
Transverse flow : Fracture	970	%	ISO 37
Flow : Fracture	460	%	ISO 37
Tear Strength ⁴			ISO 34-1
Transverse flow	46	kN/m	ISO 34-1
Flow	44	kN/m	ISO 34-1
Compression Set ⁵			ISO 815
23°C, 22 hr	22	%	ISO 815
70°C, 22 hr	37	%	ISO 815
90°C, 70 hr	61	%	ISO 815

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air ⁶			ISO 188
Transverse flow : 110°C, 1008 hr	-1.9	%	ISO 188
Flow : 110°C, 1008 hr	10	%	ISO 188
Transverse flow : 100% strain 110°C, 1008 hr	13	%	ISO 188
Flow : 100% strain 110°C, 1008 hr	-2.6	%	ISO 188
Change in Tensile Strain at Break in Air ⁷			ISO 188
Transverse flow : 110°C, 1008 hr	-3.5	%	ISO 188
Flow : 110°C, 1008 hr	14	%	ISO 188
Change in Shore Hardness in Air
Shao A, 110°C, 1008 hr ⁸	-0.40		ISO 188
Shao A, 110°C, 1008 hr ⁹	-0.50		ISO 188

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 206 sec^-1)	617	Pa·s	ASTM D3835

Legal statement
The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Legal statement

The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Injection	Nominal Value	Unit
Rear Temperature	227 - 249	°C
Middle Temperature	227 - 249	°C
Front Temperature	227 - 249	°C
Nozzle Temperature	227 - 249	°C
Processing (Melt) Temp	227 - 249	°C
Mold Temperature	16 - 32	°C
Injection Pressure	1.38 - 6.89	MPa
Injection Rate	Fast
Back Pressure	0.172 - 0.862	MPa
Screw Speed	50 - 120	rpm
Cushion	3.81 - 25.4	mm

Injection instructions
Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C).

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	216 - 238	°C
Cylinder Zone 2 Temp.	216 - 238	°C
Cylinder Zone 3 Temp.	216 - 238	°C
Cylinder Zone 4 Temp.	216 - 238	°C
Cylinder Zone 5 Temp.	216 - 238	°C
Die Temperature	216 - 238	°C

Extrusion instructions
Screw Speed: 30 to 100 rpm

Note Message
1 .	Type 1, 510mm/min
2 .	Type 1, 510mm/min
3 .	Type 1, 510mm/min
4 .	B method, right angle specimen (without cut), 510mm/min
5 .	Type a
6 .	Type 1
7 .	Type 1
8 .	1 sec
9 .	15 sec

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Teknor Apex Company
Trademark:	Sarlink® TPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LfwQ2E_SarlinkTPEFM2676PRELIMINARYDATA.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 304 TFE 5	RTP Company	PC	RTP
Ferro PP TPP20AE03UL-WH	Ferro Corporation	PP, Unspecified	Ferro PP
Fusabond® A560	DuPont Packaging & Industrial Polymers	EA	Fusabond®
Luran® S 796M	Styrolution	ASA	Luran® S
Osterlene® HIPS0302	Osterman & Company	PS (HIPS)	Osterlene®