LNP™ THERMOTUF™ PX95726 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LfSFm0_LNP-THERMOTUF-PX95726-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOTUF* PX95726 is a compound based on Nylon 6 resin containing Proprietary Filler(s). Added features of this material include: Heat Stabilized, High Impact. Also known as: LNP* THERMOTUF* Compound PDX-P-95726 Product reorder name: PX95726 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.60 | % | |
| Across Flow : 24 hr | 0.80 to 1.1 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 1.1 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5840 | MPa | ASTM D638 |
| -- | 5800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 111 | MPa | ASTM D638 |
| Yield | 109 | MPa | ISO 527-2/5 |
| Break | 107 | MPa | ASTM D638 |
| Break 3 | 108 | MPa | ASTM D638 |
| Break | 105 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.1 | % | ASTM D638 |
| Yield | 3.1 | % | ISO 527-2/5 |
| Break 5 | 3.7 | % | ASTM D638 |
| Break | 3.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4960 | MPa | ASTM D790 |
| -- | 5030 | MPa | ASTM D790 |
| -- 7 | 4790 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 171 | MPa | ASTM D790 |
| -- | 160 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 173 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 68 | J/m | ASTM D256 |
| 23°C 9 | 6.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 880 | J/m | ASTM D4812 |
| 23°C 10 | 53 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.3 | J | ASTM D3763 |
| -- | 2.60 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 214 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 201 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 191 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.4E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBB0061 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| Stanyl® TW200F6 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| TOTAL Polystyrene Crystal 1050 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Network Polymers PC 1514 UV | Network Polymers, Inc. | PC | Network Polymers PC |
| Huaxia Shenzhou FKM 246D | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |