BLUESTAR® PBT 201-G25202
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Nantong Zhonglan Engineering Plastics Co., Ltd. |
| Trademark: | BLUESTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LeG0BG_BLUESTAR-PBT-201-G25202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BLUESTAR® PBT 201-G25202 is a Polybutylene Terephthalate (PBT) product filled with 25% glass fiber. It is available in Asia Pacific or North America. Applications of BLUESTAR® PBT 201-G25202 include electrical/electronic applications and lighting applications. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | |
| Across Flow | 0.80 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.17 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 110 | MPa | ASTM D638 |
| Flexural Modulus | 7500 | MPa | ASTM D790 |
| Flexural Strength | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 9.00 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact (Area) (23°C) | 55.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 216 | °C | |
| 1.8 MPa, Unannealed | 206 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.3E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TO 137 | Mitsubishi Chemical Performance Polymers, Inc. | SBS | tefabloc® |
| Vinnolit® S 3160 | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Exxtral™ Performance Polyolefin CNR012 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Formolon® 676 | Formosa Plastics Corporation, U.S.A. | PVC, Flexible | Formolon® |
| HONES® PA66 G25 | Guangdong Shunde Hones Polymer Material Co., Ltd. | Nylon 66 | HONES® |