3M™ Dyneon™ Fluoroelastomer FE 5623

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Lcg9tb_3MDyneonFluoroelastomerFE5623.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FE 5623 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE 5623 has an incorporated bisphenol cure system. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Process targets: injection and transfer moulding, extrusion and calendering Proprietary incorporated cure technology Improved cure technology resulting in more consistent part size from successive moulding cycles Faster curing version of 3M™ Dyneon™ Fluoroelastomer FE 5620Q Improved scorch resistance at high moulding temperatures Excellent mould release - can be used in automated injection moulding equipment Clean running Compounds prepared from Dyneon FE 5623 can be formulated to meet Mil-R-83248 Typical Applications 3M™ Dyneon™ Fluoroelastomer FE 5623 is suitable for usage in injection moulding (e.g. production of O-rings) and extrusion applications.

Message

3M™ Dyneon™ Fluoroelastomer FE 5623 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE 5623 has an incorporated bisphenol cure system.

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Process targets: injection and transfer moulding, extrusion and calendering

Proprietary incorporated cure technology

Improved cure technology resulting in more consistent part size from successive moulding cycles

Faster curing version of 3M™ Dyneon™ Fluoroelastomer FE 5620Q

Improved scorch resistance at high moulding temperatures

Excellent mould release - can be used in automated injection moulding equipment

Clean running

Compounds prepared from Dyneon FE 5623 can be formulated to meet Mil-R-83248

Typical Applications
3M™ Dyneon™ Fluoroelastomer FE 5623 is suitable for usage in injection moulding (e.g. production of O-rings) and extrusion applications.

General Information
Features	Good demoulding performance
Uses	O-rings
Agency Ratings	MIL R-83248
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Extrusion Resin transfer molding Calendering Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	24	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	78		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	6.50	MPa	ASTM D412A
Tensile Strength ²	15.0	MPa	ASTM D412A
Tensile Elongation ³(Break)	190	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	19	%	ASTM D1414
200°C, 70 hr ⁵	18	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
MIDILENA III HDPE 5000S	ROMPETROL PETROCHEMICALS S.R.L.	HDPE	MIDILENA III
SLOVALEN® PH 91 GF 15	Plastcom	PP, Unspecified	SLOVALEN®
Ferro PP LPP30BD18BL	Ferro Corporation	PP Homopolymer	Ferro PP
EPLAMID 66 GX2 20 NC	EPSAN Plastik SAN. ve TiC. A.S.	Nylon 66	EPLAMID 66
Sylvin 2907-93 Clear	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin