Epoxies, Ect. 10-3020

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	Epoxies, Etc.
Trademark:	Epoxies, Ect.
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LcbDMo_Epoxies-Ect-10-3020.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

20 minute set epoxy

These high bond strength adhesives are clear 100% solids, two component, low viscosity adhesives with a quick setting time of 5-46 minutes at room temperature. They are excellent for bonding plated metals, pewter, glass, wood, ceramic, felt, cement, gem stones, most plastics and rubbers, etc...

These adhesives were tested in our laboratory for flame retardancy properties. According to our test results they meet the requirements of UL94HB.

Applications:

These unique adhesives are ideally suited for a wide range of electronic, electrical, industrial, structural, and jewelry applications. These adhesives are also an excellent choice for field repairs. They are offered in the popular TriggerBond® dual barrel cartridge dispensing system and bulk packaging.

Features:

High bond strength

Fast room temperature cure - three speeds to choose from

Water and chemical resistance

Outstanding thermal shock resistance

1:1 mix ratio

Impact resistance

General Information
Features	Bondability Fast Cure Flame Retardant Good Adhesion Good Chemical Resistance Good Impact Resistance Good Thermal Shock Resistance Low to No Water Absorption Low Viscosity
Uses	Adhesives Bonding Electrical/Electronic Applications Industrial Applications Jewelry Structural Parts
Appearance	Clear/Transparent

Impact	Nominal Value	Unit
Notched Izod Impact	140	J/m

Thermal	Nominal Value	Unit
CLTE - Flow	6.0E-5	cm/cm/°C

Thermoset	Nominal Value	Unit
Thermoset Mix Viscosity (25°C)	12000	cP

Additional Information	Nominal Value	Unit
Handle Time (25°C)	30.0 to 35.0	min
Operating Temperature	-50.0 to 130	°C

Uncured Properties	Nominal Value	Unit
Color	Clear/Transparent
Mix Ratio by Weight (PBW)
Part A	1.0
Part B	1.0
Solids Content	100	%
Density (25°C)	1.15	g/cm³
Curing Time (25°C)	24 to 48	hr
Pot Life (25°C)	10 to 15	min

Cured Properties	Nominal Value	Unit
Shore Hardness (Shore D)	72
Compression Strength	58.6	MPa
Electric Strength	17	kV/mm
Relative Permittivity (1 kHz, 25°C)	4.00
Volume Resistivity (25°C)	2.0E+14	ohms·cm
Dissipation Factor (1 kHz)	0.017

Resin Grade	Manufacturer	Category	Trademark
Unipren® Elastomers A3 PRTA010 45A EG06S1 UP326	Petropol Industry and Trade of Polymers LTDA	TPE	Unipren® Elastomers
LUVOCOM® 1100-7890 VP	Lehmann & Voss & Co.	PESU	LUVOCOM®
Lupoy® NF1007F 10R	LG Chem Ltd.	PC	Lupoy®
ADENE® O07MFBG-00	A.D. Compound S.p.A.	PP Copolymer	ADENE®
Sylvin 8205-75UV Brown 7479	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin