Lupoy® GN5007FL
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LcAMHL_Lupoy-GN5007FL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupoy®GN5007FL is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lupoy®The main features of the GN5007FL are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 61.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 740 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 119 | °C | ASTM D648 |
| Vicat Softening Temperature | 134 | °C | ASTM D1525 5 |
| RTI Elec | 95.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI | 95.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 260 - 300 | °C | |
| Middle Temperature | 250 - 290 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 260 - 290 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Back Pressure | 0.981 - 3.92 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Malen E FABS 23-D022 | LyondellBasell Industries | LDPE | Malen |
| BULKSAM® TM-25 | UMG ABS, Ltd. | ABS | BULKSAM® |
| Infino XP-2150IM | SAMSUNG SDI CO., LTD. | PPS | Infino |
| LEXAN™ HFD1910 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LEXAN™ 101R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |