ASTAMID™ MB3G8HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Lc31po_ASTAMID-MB3G8HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAMID™ MB3G8 HS is a highly heat stabilised 40% glass fibre reinforced Polyamide 6 grade. ASTAMID™ MB3G8 HS has been developed for structural applications within the automotive sector. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.43 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | -- | % | ASTM D955 |
| Water Absorption | ||||
| Saturation, 23°C | 5.7 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 13000 | 8200 | MPa | ASTM D638 |
| Tensile Strength 2(3.20 mm) | 205 | 135 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 3.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 10500 | 7400 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 280 | 200 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 6 | 20 | 30 | kJ/m² | ISO 179 |
| Notched Izod Impact (3.20 mm) | 180 | 250 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | -- | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 215 | -- | °C | |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 255 to 265 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 275 to 285 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 130 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 5.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® BP2000 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| Moplen HP422H | LyondellBasell Industries | PP Homopolymer | Moplen |
| Titacon® GB925 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Electrafil® PC/ABS 830 SS7 BK | Techmer Engineered Solutions | PC+ABS | Electrafil® |
| Kotex KGN-20MRA | Kotec Corporation | PC | Kotex |