DINALON® B1X25 G30V0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupo Repol |
| Trademark: | DINALON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | La1A9L_DINALON-B1X25-G30V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DINALON® B1X25 G30V0 is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183/A |
| Humidity 1 | < 0.25 | % | ISO 15512/B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.2 | % | ISO 527-2 |
| Flexural Modulus | 8000 | MPa | ISO 178 |
| Flexural Stress | 205 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Karl-Fischer |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 SI 5 UV | RTP Company | Nylon 66 | RTP |
| XENOY™ 5720U resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |
| Adell Polyamide AJ-17 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Elastron® G G300.A50.N | Elastron USA, Inc. | SEBS | Elastron® G |
| INFUSE™ 9807 | The Dow Chemical Company | OBC | INFUSE™ |