MonoSol® AF A127
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LZnWx4_MonoSol-AF-A127.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol AF A127 is a PVOH based thermoplastic film, soluble in hot water and manufactured using MonoSol AF's proprietary blown film technology. MonoSol AF A127 is a special grade of PVOH hot water-soluble packaging film with excellent cold water resistance and used for laundry bags and maternity units where the linen is significantly contaminated with body fluids. It is soluble in water above 65 C with agitation. Available thickness range is 22 micron (0.9 mil) to 50 micron (2.0 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 5.4 | wt% | |
| Solubility | |||
| Disintegration : 60°C, 22.9 µm 2 | 13.0 | sec | |
| Disintegration : 70°C, 22.9 µm 3 | 1.0 | sec | |
| Dissolution : 60°C, 22.9 µm 4 | 600.0 | sec | |
| Dissolution : 70°C, 22.9 µm 5 | 17.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (38.1 µm) | 19.9 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 22 | µm | |
| Film Thickness - Recommended / Available | 25 µm, 38 µm, 51 µm, and 76 µm | ||
| Secant Modulus | ASTM D882, ISO 527-3 | ||
| 10%, MD : 22 µm | 159 | MPa | |
| 100%, MD : 22 µm | 35.2 | MPa | |
| 10%, TD : 22 µm | 117 | MPa | |
| 100%, TD : 22 µm | 20.7 | MPa | |
| Tensile Strength | |||
| MD : Break, 22 µm | 35.9 | MPa | ASTM D882 |
| TD : Break, 22 µm | 34.5 | MPa | ASTM D882 |
| MD : 22 µm | 35.9 | MPa | ISO 527-3 |
| TD : 22 µm | 34.5 | MPa | ISO 527-3 |
| Tensile Elongation | ASTM D882, ISO 527-3 | ||
| MD : Break, 22 µm | 110 | % | |
| TD : Break, 22 µm | 340 | % | |
| Dart Drop Impact (38 µm) | 390 | g | ASTM D1709, DIN 53433 |
| Elmendorf Tear Strength - MD | |||
| -- | 1100 | g | ASTM D1922 |
| -- | 0.11 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| 3 . | Distilled Water (MSTM 205) |
| 4 . | Distilled Water (MSTM 205), 75% dissolved |
| 5 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo PE M8060 | Sumitomo Chemical Asia | HDPE | Sumitomo PE |
| NANCAR® 1031 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| HIPOLEN P® MA 11 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| Latistat 66-06 | LATI S.p.A. | Nylon 66 | Latistat |
| Plaskon CMU-870-2B | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |