DENIBLEND F
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Vamp Tech |
| Trademark: | DENIBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LY6vlv_DENIBLEND-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC / ABS, not Flame Retardant compound, good mechanical properties, very good impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 40 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 115 | °C | ASTM D1525 1 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5420 | Spartech Polycom | PP, Unspecified | Spartech |
| Wellamid® MRGF25/15 42H-BKDX9 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| APEX® RM 9214 | Teknor Apex Company | PVC, Rigid | APEX® |
| Geon™ Vinyl Rigid Extrusion L0659 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Kumho ABS H2938L | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |