Makrolon® Rx1805
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LXnhZb_Makrolon-Rx1805.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 6.0 cm³/10 min; medical devices; high lipid resistance; suitable for sterilization with high-energy radiation; biocompatible according to many ISO 10993-1 test requirements; high viscosity; injection molding - melt temperature 280 - 320 °C; transparent parts for medical devices |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.66 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow | 0.60 to 0.80 | % | ISO 2577 |
| Flow | 0.60 to 0.80 | % | ISO 2577 |
| Across Flow : 2.00 mm 2 | 0.70 | % | ISO 294-4 |
| Flow : 2.00 mm 3 | 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.12 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 114 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 67.0 | MPa | |
| Break, 23°C | 75.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 6.3 | % | |
| Break, 23°C | 130 | % | |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 4(23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress 5 | ISO 178 | ||
| 3.5% Strain, 23°C | 73.0 | MPa | |
| 23°C | 98.0 | MPa | |
| Flexural Strain at Flexural Strength 6(23°C) | 7.1 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flash Ignition Temperature | 480 | °C | ASTM D1929 |
| Self Ignition Temperature | 550 | °C | ASTM D1929 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | ISO 7391-PC,M,(,,)-09-9 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7 | ISO 7391 | ||
| -30°C, Complete Break | 16 | kJ/m² | |
| 23°C, Partial Break | 80 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -60°C | No Break | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 8 | ISO 7391 | ||
| -30°C, Complete Break | 15 | kJ/m² | |
| 23°C, Partial Break | 70 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 70.0 | J | |
| 23°C | 65.0 | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 6600 | N | |
| 23°C | 5700 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 138 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 126 | °C | ISO 75-2/A |
| Glass Transition Temperature 9 | 145 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ISO 306/B50 |
| -- | 145 | °C | ISO 306/B120 |
| Ball Pressure Test (135°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 6.5E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 6.5E-5 | cm/cm/°C | |
| Thermal Conductivity 10(23°C) | 0.20 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index 11 | 27 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Pellets |
| 2 . | 60x60x2 mm, 500 bar |
| 3 . | 60x60x2 mm, 500 bar |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2 mm/min |
| 7 . | Based on ISO 179-1eA, 3 mm |
| 8 . | Based on ISO 180-A, 3 mm |
| 9 . | 10°C/min |
| 10 . | Cross-flow |
| 11 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texin® RxT65D | Covestro - PUR | TPU-Polyether | Texin® |
| Formolene® E924ND | Formosa Plastics Corporation, U.S.A. | HDPE, HMW | Formolene® |
| Dynalloy™ OBC8000-T60 | PolyOne Corporation | TPE | Dynalloy™ |
| KumhoSunny PC/ABS HAC6010FG | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Pinnacle PP 1350N | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |