Lanufene LLF 181N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Ras Lanuf Oil & Gas Processing Company (RASCO) |
| Trademark: | Lanufene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LXZ9X7_Lanufene-LLF-181N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LANUFENE LLF 181N is a linear low density polyethylene for general purpose blown film extrusion with high mechanical properties and good process-ability. LANUFENE LLF 181N contains neither slip additive nor anti-blocking agent. The film produced from this resin characteristically exhibits good toughness, and outstanding puncture resistance. LANUFENE LLF 181N is particularly suitable for blending with LLDPE and/or HDPE, Coextrusion, heavy duty bags and stretch film application. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 21.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm | 220 | MPa | |
| 1% Secant, TD : 38 µm | 260 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm | 40.0 | MPa | |
| TD : Break, 38 µm | 32.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm | 750 | % | |
| TD : Break, 38 µm | 700 | % | |
| Dart Drop Impact (38 µm) | 150 | g | ASTM D1709A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm) | 53 | ASTM D2457 | |
| Haze (38.0 µm) | 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 4345S | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Borealis PP HG385MO | Borealis AG | PP Homopolymer | Borealis PP |
| Ferro PP LPP20BN39AL | Ferro Corporation | PP, Unspecified | Ferro PP |
| LEXAN™ FXD171R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Karina BLACK PVC COMPOUND 900-DA-48/ 1-C-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |