Fire PRF2 1000 FM
| Category: | PF , Phenol Formaldehyde Resin |
| Manufacturer: | Indspec Chemical Corporation |
| Trademark: | Fire PRF2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LX9xKm_Fire-PRF2-1000-FM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fire PRF2 1000 FM is a Phenol Formaldehyde Resin (PF) product filled with glass fiber. It is available in North America. Typical application: Construction Applications. Primary characteristic: flame retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7580 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 110 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 1.0 | % | |
| Break | 2.2 | % | |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 860 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 52 | % | ASTM D2863 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 3.0 Mix Ratio by Weight: 34 | ||
| Resin | Mix Ratio by Weight: 46 Mix Ratio by Volume: 4.0 | ||
| Pot Life (23°C) | 10 to 20 | min | |
| Shelf Life (22°C) | 26 | wk | |
| Thermoset Mix Viscosity (23°C) | 750 | cP | ASTM D2393 |
| Demold Time | |||
| 23°C | 1400 | min | |
| 32°C | 60 to 120 | min | |
| 52°C | 30 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP251 | Southern Polymer, Inc. | PP Impact Copolymer | PRIMALENE |
| Allen ABS ULG/499 | SEKISUI Polymer Innovations, LLC | ABS | Allen ABS |
| LARIPUR® LPR 72D25 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| Polaris™ C 80355-13 | Ashland Performance Materials | Polyester, TS | Polaris™ |
| RTP 199 X 142473 A | RTP Company | PP, Unspecified | RTP |