SEQUEL® 1718-FP HO
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | SEQUEL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LX35hx_SEQUEL-1718-FP-HO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sequel 1718-PF HO thermoplastic polyolefin is designed for painted automotive exterior applications that require dimensional stability over a broad temperature range. This material exhibits excellent processability and low-temperature properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 20.0 | MPa | ASTM D638 |
| Yield, 23°C | 20.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| 23°C 2 | 1590 | MPa | ASTM D790 |
| 23°C 3 | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Impact (-30°C) | 24.8 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 89.0 | °C | ASTM D648, ISO 75-2/B |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HMN TR-942 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| RTP 206 K | RTP Company | PARA | RTP |
| Catalyst CT/2-HP | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Forprene® 6NE001A65 | SO.F.TER. SPA | TPV | Forprene® |
| OTECH PVC OM5830-Soles | OTECH Corporation | PVC, Unspecified | OTECH PVC |