SCHULADUR® A1 GF 30 LW
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LU5xL1_SCHULADUR-A1-GF-30-LW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fibre reinforced, laser weldable PBT/PET blend |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 24.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 9700 | MPa | ISO 178 |
| Flexural Stress 2 | 200 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 2.5 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 44 | kJ/m² | ISO 179/1eU |
| 23°C | 48 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 210 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 190 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ISO 306/A50 |
| -- | 192 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | 55 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.60 mm | HB | IEC 60695-11-10, -20 | |
| 3.20 mm | HB | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 675 | °C | IEC 60695-2-12 |
| 3.00 mm | 675 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 700 | °C | IEC 60695-2-13 |
| 3.00 mm | 700 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1985NT | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| BULKSAM® TM-25M | UMG ABS, Ltd. | ABS | BULKSAM® |
| Celanex® XFR 4840 | Celanese Corporation | PBT | Celanex® |
| CP PRYME® Polypropylene PPC100/2I-20M NAT | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| Zytel® 73G40T BK416 | DuPont Performance Polymers | Nylon 6 | Zytel® |