Borealis PE HE3366
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LTWbK3_Borealis-PE-HE3366.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
It is a HDPE compound for solid insulation of telephone singles with high extrusion speed. HE3366 is designed as insulation for petroleum filled telephone cables. It is also suitable as outer skin in "foam-skin" cosntructions. HE3366 meets the applicable requirements below using sound commercial extrusion practice and testing procedures:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.945 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (50°C, 10% Igepal, F20) | > 48.0 | hr | IEC 60811-4-1/B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 600 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Oxidation Induction Time (200°C) | 50 | min | IEC 60811-410 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 22 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 2.33 | IEC 60250 | |
| Dissipation Factor | 6.0E-5 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 165 - 230 | °C | |
| Melt Temperature | 220 - 250 | °C | |
| Die Temperature | 230 | °C |
| Extrusion instructions |
|---|
| Conductor preheating temperature: 100 to 120 °CCooling water: 50 °C |
| Note Message | |
|---|---|
| 1 . | ISO 1872-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LDM 733 | Marco Polo International, Inc. | LDPE | MARPOL® |
| Comai 408-2 NT | Comai Ltda | PP Copolymer | Comai |
| Karina CLEAR PVC COMPOUND 70/201-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina RED COLOR CONCENTRATE -E 42/129-RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LONGLITE® PBT 3010-200X | CCP Group | PBT | LONGLITE® PBT |