DOWLEX™ NG 5066G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LSyOg8_DOWLEX-NG-5066G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™NG 5066G polyethylene resin is an ethylene-octene -1 copolymer, which is suitable for the production of blown films. These blown films require good tear strength and excellent toughness as well as good stiffness and high and low temperature resistance. Typical applications include composite films. Application field:
Meet the following regulatory requirements:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.934 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.7 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 2% secant, MD : 50 µm | 420 | MPa | ISO 527-3 |
| 2% secant, TD : 50 µm | 470 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm | 14.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm | 17.0 | MPa | ISO 527-3 |
| MD : Break, 50 µm | 21.0 | MPa | ISO 527-3 |
| TD : Break, 50 µm | 23.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 590 | % | ISO 527-3 |
| TD : Break, 50 µm | 620 | % | ISO 527-3 |
| Dart Drop Impact (50 µm) | 110 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 130 | g | ASTM D1922 |
| TD : 50 µm | 230 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 240 | °C |
| Extrusion instructions |
|---|
| 制造条件： 模具间隙 2.5 mm 熔体温度：190 至 240°C 放大比：1.5 至 3:1 建议的厚度范围：10 至 150 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aegis® H135ZP | Honeywell | Nylon 6 | Aegis® |
| Braskem PP KN-501 | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| HiFill® POM CO GF15 CC | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Hostacom PPR 1042 HL21S | LyondellBasell Industries | PP Copolymer | Hostacom |
| KumhoSunny PPO HSP8340 | Shanghai KumhoSunny Plastics Co., Ltd. | PPE+PS | KumhoSunny PPO |