Latilub 66-10T Y/15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LSxSZl_Latilub-66-10T-Y-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-lubricating product based on Polyamide 66 (PA 66). PTFE. Aramid fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.4 to 1.7 | % | |
| Flow : 2.00 mm | 1.3 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 5.0 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D3702 | ||
| vs. Itself - Dynamic | 0.21 | ||
| vs. Itself - Static | 0.25 | ||
| Wear Factor | 7.50E-10 | (m³/h)/(N·m·h) | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 40 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 245 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVADURAN® 5010R3-2 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Hanwha Total PP BI990 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| LGG 108 | LG Polymers India Pvt. Ltd. | PS (GPPS) | LGG |
| POLYelast TPE 10012 R3 | Polykemi AB | PP+EPDM | POLYelast |
| LEXAN™ EXL1132 resin | SABIC Innovative Plastics | PC | LEXAN™ |