Propafilm™ RHX200
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LSsApH_Propafilm-RHX200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Heavy Duty Barrier Coated Film Biaxially oriented polypropylene (BOPP) film coated on both sides with an aqueous dispersion of polyvinylidene chloride (PVdC) copolymer. RHX200 is suitable for use as a single web replacement of laminations. Particularly suited to vertical form-fillseal applications in the confectionery industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 121°C, 1 min | 4.0 | % | |
| Flow : 129°C, 1 min | 7.0 | % | |
| Across Flow : 129°C, 1 min | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.25 | ||
| vs. Itself - Static, Outside/Outside | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 5100 | µm | |
| Seal Strength 1 | 0.14 | N/mm | Internal Method |
| Seal Initiation Temperature 2 | 93.3 to 146 | °C | Internal Method |
| Oxygen Permeability (23°C, 0% RH) | 0.43 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 3.3 | g/m²/24 hr | ASTM F1770 |
| Yield | 20.1 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 110 | ASTM D2457 | |
| Haze 3 | 2.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 225°F; 1sec; 15lb/in² |
| 2 . | 2secs; 15psi |
| 3 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niuk 40NE00 | Shanghai Niuk New Plastic Technology Co., Ltd. | Nylon 6 | Niuk |
| Bynel® 41E556 | DuPont Packaging & Industrial Polymers | LLDPE | Bynel® |
| Kumho EP HSP 8344 | Korea Kumho Petrochemical Co., Ltd. | PPE+PS | Kumho EP |
| INELEC PA66CF10IM | Infinity LTL Engineered Compounds | Nylon 66 | INELEC |
| Celstran® PP-GF50-04 Black | Celanese Corporation | PP, Unspecified | Celstran® |