Halene H B5500
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LRzg9r_Halene-H-B5500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
B5500 is a HM-HDPE Blow Molding Grade, produced by the Mitsui CX Process. This resin is particularly recommended for medium to Large Bulk Containers (~ 120 liter) for Chemicals, Detergent or Lube Oils. B5500 combines exceptional processability with high rigidity, excellent mechanical properties and impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.956 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 8.0 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.35 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield, molding | 28.0 | MPa | ASTM D638 |
| Fracture, molding | 40.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, molding | 10 | % | ASTM D638 |
| Fracture, molding | 1000 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 1000 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 4 |
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 210 | °C | |
| Cylinder Zone 3 Temp. | 215 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Die Temperature | 200 - 210 | °C |
| Extrusion instructions |
|---|
| Parison Temperature: 190 to 210°CCooling Water for Mold: 20 to 25°C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ POL051G20L | ACLO Compounders Inc. | PC | ACCUTECH™ |
| ColorFast® FRA204 | LTL Color Compounders, Inc. | ABS | ColorFast® |
| OTECH TPE OTO7510EP1 - A/V Jacket | OTECH Corporation | TPE | OTECH TPE |
| Neoflex™ 7070 | Zylog Plastalloys Pvt. Ltd. | TPE | Neoflex™ |
| Sylvin 4200-85 Grey 9572 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |