LNP™ THERMOCOMP™ 2X00858 compound
| Category: | FEP , Perfluoroethylene Propylene Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LRYF9u_LNP-THERMOCOMP-2X00858-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 2X00858 is a compound based on FEP resin containing proprietary fillers. Also known as: LNP* THERMOCOMP* Compound PDX-FP-F-00858 Product reorder name: 2X00858 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 2.16 | g/cm³ | |
| -- | 2.17 | g/cm³ | |
| Water Absorption (24 hr, 50% RH) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1010 | MPa | ASTM D638 |
| -- | 939 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 14.0 | MPa | ASTM D638 |
| Yield | 14.0 | MPa | ISO 527-2/5 |
| Break 3 | 12.0 | MPa | ASTM D638 |
| Break | 13.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.5 | % | ASTM D638 |
| Yield | 6.1 | % | ISO 527-2/5 |
| Break 5 | 9.3 | % | ASTM D638 |
| Break | 9.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 797 | MPa | ASTM D790 |
| -- 7 | 873 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 19.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 20.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 680 | J/m | ASTM D256 |
| 23°C 9 | 32 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 980 | J/m | ASTM D4812 |
| 23°C 10 | 85 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 79.3 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 80.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 57.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 61.0 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Roscom PVC 720-75 | Roscom, Inc. | PVC, Flexible | Roscom PVC |
| THERMOLAST® K TC4LEZ (Series: UV/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| AKROMID® A3 GF 13 S1 natural (2167) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Lanufene HDF-5116 | Ras Lanuf Oil & Gas Processing Company (RASCO) | HDPE | Lanufene |
| Rotuba CAB B902 (10% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |