Surlyn® 8940
| Category: | EMAA , Ethylene Methacrylic Acid |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Surlyn® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LPGguA_Surlyn-8940.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Surlyn® 8940 is a sodium ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 8940 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.8 | g/10 min | ASTM D1238, ISO 1133 |
| Ion Type | Sodium |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance - NBS Index | 370 | ASTM D1630 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Freezing Point | |||
| -- | 59 | °C | ASTM D3418 |
| -- | 59 | °C | ISO 3146 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 33.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 470 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | ASTM D790 | ||
| -20°C | 717 | MPa | |
| 23°C | 350 | MPa | |
| Flexural Strength (Yield) | 15.0 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (23°C) | 1.48 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 1000 | J/m | ASTM D256 |
| Tensile Impact Strength | ASTM D1822 | ||
| -40°C | 757 | kJ/m² | |
| 23°C | 1020 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -106 | °C | ASTM D746 |
| Vicat Softening Temperature | 63.0 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 94.0 | °C | ASTM D3418, ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (6350 µm) | 5.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 185 to 285 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 F SI 2 | RTP Company | Nylon 12 | RTP |
| Radilon® S RV400K 333 NER | Radici Plastics | Nylon 6 | Radilon® |
| Bayblend® FR3010 IF | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| DOMAMID® 6STZ | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Lushan RF1000 | Guangzhou Lushan New Materials Co., Ltd | PE, Unspecified | Lushan |