LubriOne™ LB 6600-5011 RS Natural
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LN3l48_LubriOne-LB-6600-5011-RS-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Molybdenum disulfide modified, Normal heat resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 300 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16500 | MPa | ISO 527-2 |
| Tensile Strength | 230 | MPa | ISO 527 |
| Nominal Tensile Strain at Break | < 2.0 | % | ISO 527-2 |
| Flexural Strength | 305 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 95 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 220 | °C | ISO 75-2/A |
| Melting Temperature | 255 - 265 | °C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+15 | ohms | ASTM D257 |
| -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 80 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.70 | IEC 60250 | |
| Dissipation Factor | 0.050 | IEC 60250 | |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BCC Resins BC 4553 | BCC Products Inc. | Polyester, TS | BCC Resins |
| Fluoraz FEPM 790 | Greene, Tweed & Co. | FEP | Fluoraz |
| Escorene™ Ultra UL 7510 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Lumiloy® GP1000D | LG Chem Ltd. | PPE+PS | Lumiloy® |
| PENTAMID AB GV50 H black | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |