TITANLENE® LDF 204GH
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Lotte Chemical Titan (M) Sdn. Bhd. |
| Trademark: | TITANLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LMg2F5_TITANLENE-LDF-204GH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TITANLENE® LDF 204GH is a Low Density Polyethylene material. It is available in Asia Pacific for film extrusion. Important attributes of TITANLENE® LDF 204GH are:
Typical application of TITANLENE® LDF 204GH: Film |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 30 µm, Blown Film | 245 | MPa | |
| 1% Secant, TD : 30 µm, Blown Film | 284 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm, Blown Film | 22.6 | MPa | |
| TD : Break, 30 µm, Blown Film | 19.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm, Blown Film | 190 | % | |
| TD : Break, 30 µm, Blown Film | 500 | % | |
| Dart Drop Impact (30 µm, Blown Film) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, Blown Film | 260 | g | |
| TD : 30 µm, Blown Film | 170 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 30.0 µm, Blown Film) | 10 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 5.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 6013 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Thermylene® P-10FG-2100 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Fainplast PVC GSK 6515 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| D-MEC SCR11120 | D-MEC Ltd. | Epoxy | D-MEC |
| KUBE PIR 21820 | KUBE Electronics AG | HDPE | KUBE PIR |