Tecnoprene® VK10 NERO900
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Tecnoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LGnEG8_Tecnoprene-VK10-NERO900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer, 50% glass fibre reinforced |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.25 | % | Internal Method |
| Ash Content | 50 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 102 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 10800 | MPa | ASTM D790 |
| Flexural Strength | 175 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648 |
| Vicat Softening Temperature | 147 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 220 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT7016-00 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| REVOLVE® M-574 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| TPUCO® TPUI-ED71 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Leona™ 9400S | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Wuxi Jiahong EB-2000 | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |