| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LFrWd0_DurethanBKV30W1000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, weather stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ||||
| Vertical flow direction : 280°C, 3.00mm 1 | 0.82 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 2 hours, 3.00mm 2 | 0.12 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 3.00mm 3 | 0.16 | -- | % | ISO 2577 |
| Flow direction : 120°C, 2 hours, 3.00mm 4 | 0.030 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 210 | 100 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9800 | 6100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 180 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 7.0 | % | ISO 527-2/5 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 5100 | MPa | ISO 899-1 |
| 1000 hr | -- | 4100 | MPa | ISO 899-1 |
| Flexural Modulus 5(23°C) | 8600 | 5100 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% strain | 265 | 135 | MPa | ISO 178/A |
| 23°C | 280 | 160 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 4.0 | 7.0 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GLR, 14-100, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 8 | 6.00 | -- | J | ISO 6603-2 |
| -- 9 | 8.00 | 14.0 | J | ISO 6603-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 13 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 70 | kJ/m² | ISO 179/1eU |
| 23°C | 80 | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C | 15 | 25 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | ||||
| -- | 200 | -- | °C | ISO 306/B50 |
| -- | > 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 10 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 40 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.00 | 10.0 | IEC 60250 | |
| 23°C, 1 MHz | 4.00 | 4.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 5.0E-3 | 0.20 | IEC 60250 | |
| 23°C, 1 MHz | 0.015 | 0.12 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 600 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 11 | 22 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x3; MT 80°C; 500 Bar |
| 2 . | 150x150x3 |
| 3 . | 150x150x3; MT 80°C; 500 Bar |
| 4 . | 150x150x3 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | -30°C |
| 9 . | 23°C |
| 10 . | 10°C/min |
| 11 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XWB-3330 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| 4LAC® 25H20500 | 4Plas | ABS | 4LAC® |
| Bapolene® 200F | Bamberger Polymers, Inc. | LDPE | Bapolene® |
| CALIBRE™ 301EP-22 | Trinseo | PC | CALIBRE™ |
| Formolene® 3355O | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |