LUBEMID B27 MB NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LEpAT5_LUBEMID-B27-MB-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA6 first choice. Lubricated with Molibdenum disulphide. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 to 1.16 | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr, 3.20 mm) | 2.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 to 4000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 50.0 to 60.0 | MPa | |
| Break | 50.0 to 60.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 8.0 to 10 | % | |
| Break | 15 to 20 | % | |
| Flexural Modulus 1 | 3000 to 3500 | MPa | ISO 178 |
| Flexural Stress 2 | 70.0 to 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 to 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 to 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 35 to 45 | J/m | ASTM D256A |
| 23°C 3 | 100 to 110 | kJ/m² | ASTM D256 |
| 23°C | 4.0 to 5.0 | kJ/m² | ISO 180/A |
| 23°C 4 | 3.5 to 4.5 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 90 to 100 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 115 to 165 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 160 to 170 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 55.0 to 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 205 to 215 | °C | ISO 306/A120 |
| -- | 200 to 210 | °C | ISO 306/B120 |
| Melting Temperature | 210 to 225 | °C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 128 HI Z | RTP Company | PP, Unspecified | RTP |
| RTP 300 MG 30 | RTP Company | PC | RTP |
| TECHNO ABS F5450 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Daicel PP PT3N1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Latishield 75/4-10A | LATI S.p.A. | PBT | Latishield |