Hostacom X G3 U10 100001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LDeq3t_Hostacom-X-G3-U10-100001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom X G3 U10 is a 30% glass coupled PP homopolymer with high flow, high stiffness, low creep under load at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 140 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/A50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRILITE AC3800 | Formosa Plastics Corporation | PC | TAIRILITE |
| LNP™ LUBRICOMP™ GFL36L compound | SABIC Innovative Plastics | PSU | LNP™ LUBRICOMP™ |
| MACOMASS TPE MM-TPE O 1451 | MACOMASS Verkaufs AG | TPE | MACOMASS TPE |
| Sylvin 6227-83 Blue 8461 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ RF0069XZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |