Styrolution PS 542N
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolution PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LD4WUe_Styrolution-PS-542N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Styrolution PS 542N is an impact polystyrene with high heat resistance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 4.10 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | < 0.10 | % | |
| Equilibrium, 23°C, 50% RH | < 0.10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1750 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 1.8 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 45 | % | ISO 527-2 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 92.0 | °C | ASTM D1525 1 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.16 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+18 | ohms·cm | IEC 60093 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 260 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RV300RKC 106 NAT | Radici Plastics | Nylon 66 | Radilon® |
| TUFNYL® SGF 30 MILKY WHITE | SRF Ltd. | Nylon 6 | TUFNYL® |
| VALOX™ 4631 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| Karina BLACK PVC COMPOUND 880-48/ 1-F-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8036-75 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |