Lupoy® GP5100
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LCSk9g_Lupoy-GP5100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupoy® GP5100 is a Polycarbonate + ABS (PC+ABS) material filled with 10% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 to 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 88.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 6.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 49000 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 137 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 121 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 95.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 250 to 265 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 235 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.0196 to 0.0588 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badamid® LA70 H | Bada AG | Nylon 66 | Badamid® |
| KOPA® KN333G30HS | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Huafon JF-W-AL6030 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Kynar Flex® 2850 WR | Arkema | PVDF | Kynar Flex® |
| Lifoflex® UVX 58.01 B045-3 | ELASTO | TPE | Lifoflex® |