Kinta FR2600
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kinta Technology (Hong Kong) Co., Ltd. |
| Trademark: | Kinta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L9XnMz_KintaFR2600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kinta FR2600 is a polypropylene product,. It is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.60 - 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 15 | % | ASTM D638 |
| Flexural Modulus 3 | 1980 | MPa | ASTM D790 |
| Flexural Strength 4 | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 4.20 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 70.0 | °C | ASTM D648 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 43 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75 - 80 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 200 - 205 | °C | |
| Middle Temperature | 200 - 210 | °C | |
| Front Temperature | 200 - 205 | °C | |
| Nozzle Temperature | 205 - 210 | °C | |
| Processing (Melt) Temp | 198 - 210 | °C | |
| Mold Temperature | 90 - 100 | °C | |
| Injection Pressure | 100 - 130 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PS 3124 70/35 | MBA Polymers | PS (GPPS) | MBA PS |
| Vi-Chem PVC VNC107E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| NEXT SIGNATURE PBT G30-300 | NEXT Specialty Resins, Inc. | PBT | NEXT SIGNATURE |
| ALCOM® PA66 910/1.2 CF30 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| HIVAL® FL23 020 AC MM | Nexeo Solutions, LLC. | LDPE | HIVAL® |