LNP™ LUBRICOMP™ ZP001XXP compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L9OrsP_LNPLUBRICOMPZP001XXPcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ZP001XXP is a compound based on PPE+PS Blend resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound ZL-4510 Product reorder name: ZP001XXP |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2350 | MPa | ASTM D638 |
| Tensile Strength (Break) | 42.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 21 | % | ASTM D638 |
| Flexural Modulus | 2480 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 500 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 119 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 15 HI | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| SILVER® PA540G30N | Guangdong Silver Age Sci & Tech. Co., Ltd | Nylon 6 | SILVER® |
| Ultramid® B33 L | BASF Corporation | Nylon 6 | Ultramid® |
| Zytel® HTN FR52G30BL NC010 | DuPont Performance Polymers | PPA | Zytel® HTN |
| DynaMix Lite™ 1144-P | Polymer Dynamix | ABS | DynaMix Lite™ |