Vipel® F701-SPT-15
| Category: | Polyester Alloy , Polyester Alloy |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L9KzHR_Vipel-F701-SPT-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vipel Corrosion Resistant Isophthalic Polyester Resin AOC's Vipel F701-S series resins are high molecular weight, two stage isophthalic, unsaturated polyester resins with the wet out, cure and handling characteristics of general purpose resins. The main feature is lower styrene content. They have an excellent shelf life and are ideal for filament winding and spray-up. A few selected resins are listed below. Corrosion resistance AOC's Vipel F701-S series resins provide excellent corrosion resistance when used in contact with inorganic and organic acids. Solvent resistance is field-proven for many petroleum products such as kerosene, heating oil and crude oils. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Vipel F701-S series resins contain less styrene than standard versions. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up, filament winding, etc. Food and Drug All resins in this datasheet are manufactured from raw materials that are listed in FDA regulation Title 21 CFR 177.2420. It is the fabricator's responsibility to also be sure that the final composite is well cured. All composites used for FDA applications should be post cured at 180°F/82°C for at least 4 hours. After post curing it should be washed with soap and water and then rinsed. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | |
| Styrene Content | 42 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Exotherm | |||
| Gel to Peak | 12.0 | min | |
| Peak | 199 | °C | |
| Gel Time (25°C) 1 | 15.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Thixotropic Index 2 | 2.10 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 46 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3860 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 88.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.1 | % | ASTM D638 |
| Flexural Modulus | 4210 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 128 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity 3(25°C) | 550 | cP | |
| Post Cure Time (82°C) | 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | Gel time with 1.25% MEKP |
| 2 . | 2/20 rpm Thix Index |
| 3 . | Brookfield RV viscosity spindle 2 at 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra PBT 23 | ResMart | PBT | ResMart Ultra |
| Stanyl® TS250F6D | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Sylvin 5201-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| FORMULA P COMP 3220 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Iupiace® GV20 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |