GLAMIDE® T-665C30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L8dR4H_GLAMIDE-T-665C30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE® T-665C30 is a Polyamide 66 (Nylon 66) product filled with 30% carbon fiber. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.27 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.20 to 0.50 | -- | % | |
| 3.00 mm | 0.60 to 0.90 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.60 | -- | % | |
| Equilibrium, 65% RH | 1.7 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 260 | 235 | MPa | |
| Yield, 23°C | 216 | 150 | MPa | |
| Yield, 80°C | 132 | 105 | MPa | |
| Tensile Elongation (Break, 23°C) | 2.4 | 3.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 19000 | 17200 | MPa | |
| 23°C | 15600 | 10000 | MPa | |
| 80°C | 10000 | 7200 | MPa | |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 337 | 320 | MPa | |
| Yield, 23°C | 300 | 215 | MPa | |
| Yield, 80°C | 210 | 140 | MPa | |
| Taber Abrasion Resistance (1000 Cycles, CS-17 Wheel) | 6.00 | -- | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 72 | 80 | J/m | |
| 23°C | 120 | 150 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | -- | °C | ASTM D648 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+12 | -- | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 140 | °C | |
| Injection Pressure | 30.0 to 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILIMIX 59D2 | SILON s.ro | Siloxane, UHMW | SILIMIX |
| AT 520 | Celanese EVA Performance Polymers | LDPE | AT |
| Kemcor LD 1108 | Qenos Pty Ltd | LDPE | Kemcor |
| Polifil® Nylon 620 | The Plastics Group | Nylon 66 | Polifil® Nylon |
| Petrothene® NA324009 | LyondellBasell Industries | MDPE | Petrothene® |