Ecomann® Bioresin EM30010
| Category: | PHA , Polyhydroxyalkanoate |
| Manufacturer: | Shenzhen Ecomann Biotechnology Co., Ltd. |
| Trademark: | Ecomann® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L7gEzH_Ecomann-Bioresin-EM30010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EM30010 is semi-crystalline biodegradable, aliphatic bio-polyester designed for use in extrude tube applications. EM30010 is PHA base compound with PLA and some additives. EM30010 is certificated to meet EN13432 & ASTM D6400 standards for biodegradable plastics. Typical applications: Shampoo bottles, cosmetics bottles |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (170°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | < 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 15.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 200 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Transmission Rate (40°C, 90% RH, 130 µm) | 130 | cm³/m²/24 hr | |
| Water Vapor Transmission Rate (25°C, 90% RH, 130 µm) | 15 | g/m²/24 hr |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 70.0 | °C | ASTM D1525 1 |
| Melting Temperature | 130 to 150 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | 50 | YI | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 115 to 130 | °C | |
| Cylinder Zone 3 Temp. | 125 to 135 | °C | |
| Cylinder Zone 5 Temp. | 130 to 145 | °C | |
| Die Temperature | 115 to 130 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® C50 | Nilit Plastics | Nylon 66/6 | POLYNIL® |
| DuraGrip® DGR 6040NC | Advanced Polymer Alloys | TPE | DuraGrip® |
| Hylon® N1213STL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| POLYFLON™ D-3A | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| Moplen HP552R | LyondellBasell Industries | PP Homopolymer | Moplen |