INFUSE™ 9000
| Category: | OBC , Olefin Block Copolymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INFUSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L7XIIz_INFUSE-9000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INFUSE™ 9000 Olefin Block Copolymer is a high performance olefin block copolymer that can be widely used in thermoplastic elastomer applications where higher service temperature requirements are needed. INFUSE 9000 also provides high filler loading capability along with low compression set and good processability. Main Characteristics:
Complies with
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.877 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 71 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant (Compression Molded) | 3.29 | MPa | ASTM D638 |
| Tensile Strength (Break, Compression Molded) | 6.28 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 370 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 15.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1200 | % | ASTM D412 |
| Tear Strength | 42.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C | 23 | % | |
| 70°C | 45 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 120 | °C | Internal Method |
| TMA 1(1.00 mm) | 104 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 1N, 5°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 461 | RTP Company | PS (HIPS) | RTP |
| Michilene F8100GF20-02 | API Polymers, Inc. | PP Homopolymer | Michilene |
| FARBOSET® 5000 | Cosmic Plastics, Inc. | Epoxy | FARBOSET® |
| Iupilon® GPX2010PH | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LNP™ THERMOCOMP™ KF005 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |