Borlink™ LC8205R
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borlink™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L6UTId_Borlink-LC8205R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Borlink LC8205R is a crosslinkable natural polyethylene compound based on Supercure technology, specially designed for insulation of energy cables. Borlink LC8205R is intended for insulation of XLPE power cables with rated voltages up to 72 kV. It is designed for cable constructions with bonded insulation shields. Borlink LC8205R meets the applicable requirements as below when processed using sound extrusion practices and testing procedures
Borlink LC8205R is a ready-to-use natural co-polymer compound. It provides superior electrical performance (polymer WTR XLPE) meeting the most stringent wet ageing requirements. It offers excellent scorch resistance, long production runs and high line speed potential. Borlink LC8205R cleanliness level is assured through the Borealis quality control system. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (Base Resin) | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Moisture Content | ppm | Karl Fisher |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Properties - After Ageing 168 h (135°C) 1 | % | IEC 60811-401 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset | IEC 60811-507 | ||
| Elongation under load, 0.20 MPa : 200°C | 75 | % | IEC 60811-507 |
| Permanent deformation, 0.20 MPa : 200°C | 5.0 | % | IEC 60811-507 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Methanol Wash | ppm | Internal method | |
| Monsanto ODR | 37.0 - 47.0 | dNm | ASTM D2084 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2(Yield) | > 17.0 | MPa | ISO 527-2/250 |
| Tensile Strain 3(Break) | > 450 | % | ISO 527-2/250 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | > 22 | kV/mm | IEC 60243-1 |
| Dielectric Constant (50 Hz) | 2.30 | IEC 60250 | |
| Dissipation Factor (50 Hz) | 5.0E-4 | IEC 60250 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| The product(s) mentioned herein are not intended to be used for medical, pharmaceutical or healthcare applications and we do not support their use for such applications. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 125 - 135 | °C |
| Note Message | |
|---|---|
| 1 . | Crosslinked specimen |
| 2 . | Crosslinked specimen |
| 3 . | Crosslinked specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000/50 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| NaturePlast PLE 005 | NaturePlast | PLA | NaturePlast |
| Fainplast PVC GK 01596 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Karina STRAW PVC COMPOUND 801-38/39-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Orgalloy® LE 60ES | Arkema | Nylon 6 Alloy | Orgalloy® |