DOW™ LDPE 133A
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | L5sKNQ_DOW-LDPE-133A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 3.64 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 51 µm | 135 | J/cm³ | ASTM D882 |
| TD : 51 µm | 186 | J/cm³ | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 13.3 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 11.6 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 24.8 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 26.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 330 | % | ASTM D882 |
| TD : Fracture, 51 µm | 620 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 250 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 300 | g | ASTM D1922 |
| TD : 51 µm | 200 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 111 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 46 | ASTM D2457 | |
| Haze (50.8 µm) | 14 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 215 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆类型：单跨双混合 模具间隙：40 密尔 (1.0 mm) 熔体温度：419°F (215°C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：99 rpm 冷冻线高度：30 分钟 (762 mm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-CO-20T | Pro Polymers | PP Copolymer | Pro-Comp™ |
| RTP 3185 | RTP Company | PFA | RTP |
| WELLAMID Nylon 6000 CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Witcom PP C/2G-EC-EM | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| Hostacom HBC 327L NAT | LyondellBasell Industries | PP Homopolymer | Hostacom |